Pure & crystallized 2D Boron Nitride sheets synthesized via a novel process coupling both PDCs and SPS methods

Scientific Reports volume 6, Article number: 20388 (2016) Cite this article

3818 Accesses

25 Citations

Metrics details

Within the context of emergent researches linked to graphene, it is well known that h-BN nanosheets (BNNSs), also referred as 2D BN, are considered as the best candidate for replacing SiO2 as dielectric support or capping layers for graphene. As a consequence, the development of a novel alternative source for highly crystallized h-BN crystals, suitable for a further exfoliation, is a prime scientific issue. This paper proposes a promising approach to synthesize pure and well-crystallized h-BN flakes, which can be easily exfoliated into BNNSs. This new accessible production process represents a relevant alternative source of supply in response to the increasing need of high quality BNNSs. The synthesis strategy to prepare pure h-BN is based on a unique combination of the Polymer Derived Ceramics (PDCs) route with the Spark Plasma Sintering (SPS) process. Through a multi-scale chemical and structural investigation, it is clearly shown that obtained flakes are large (up to 30 μm), defect-free and well crystallized, which are key-characteristics for a subsequent exfoliation into relevant BNNSs.

Thanks to their remarkable potential for electronic applications, 2D-nanomaterials related researches are currently booming. Especially, hexagonal boron nitride (h-BN) is a key material in particular within the context of emergent researches linked to graphene. Indeed, it is well known that BNNSs have been considered as one of the best candidates for replacing SiO2 as dielectric support or capping layers for graphene1. The most important reason is linked to SiO2 surface imperfections (roughness, charged traps …), which can significantly limit the carriers’ mobility within graphene’s atomic sheets, then affecting their electronic transport properties. Since lattice parameters of BNNSs perfectly match the ones of graphene, this drawback should be overcome2. Recent works3,4 even present the possibility of building multi-layered hetero-structures in which h-BN and exfoliated graphene flakes are alternatively stacked to form vertically-oriented graphene-based transistors5,6.

To succeed in these domains of applications, the development of an accessible resource of pure and highly crystallized h-BN crystals remains challenging. Today, only two main sources of hexagonal boron nitride (h-BN) crystals are commonly available for the production of BNNSs after a mechanical or chemical cleavage. Firstly, commercial sources7,8, generally obtained from an oxygen-containing boron compound reacting with a nitrogen-containing source, which are most often characterized by a high level of defects with relatively small crystalline areas (from less than 2 μm up to 10 μm). Secondly, h-BN-crystals can also be found using the High Pressure High Temperature (HPHT) method adopted at the National Institute for Materials Science (NIMS Japan)9,10. This process allows the cleavage of relatively large (~100 μm) and thin (several nm) BN samples with an atomically flat surface and low defects density. However, widespread of this latter resource is hindered by its severe production conditions, e.g. high temperature (up to 2100 °C), high pressure (5.5 GPa) and treatments time (80 h). Those specificities do not allow, up to now (to our knowledge), the reproducibility of that route by other group.

In order to reach large and highly crystallized h-BN sheets, two strategies can be considered. The first one consists in a direct deposition of the required BNNSs on a substrate, while the second one is based on the generation of BNNSs by exfoliation of large h-BN single crystals.

Considering the first approach, literature reports CVD and CVD-derivatives11,12,13,14,15 syntheses of BN nanolayers deposited on different substrates using boron and nitrogen based precursors16,17,18,19. However, adopting such gaseous-based methods, it is difficult to control the defects formation and to tune the number of layers. The second approach takes advantage of the weak h-BN inter-planar force to get, by exfoliation, a two-dimensional few layers graphene-like structure (often referred as BN nanosheets). Exfoliation is well-documented in the literature and can be performed by mechanical16,20,21,22,23,24 or chemical25,26,27,28,29,30,31,32,33,34,35 methods. As a consequence, this indirect way for generating BNNSs by exfoliation from high quality h-BN crystals seems more relevant, but actually suffers from a lack of pure h-BN sources of supply, as discussed above.

Keeping this issue in mind, we propose an innovative alternative experimental procedure, which can be widely applied to produce important amount of h-BN flakes with large-scale (>10 μm) and high purity based on an original combination of two advanced techniques: the Polymer Derived Ceramics (PDCs) route and the Spark Plasma Sintering (SPS) process.

In a first step, the PDCs route is involved in the preparation of very pure preceramic polymer from a molecular resource. Among all available precursors for producing h-BN from the PDCs route, recent works have shown that polyborazylene (PBN) was the best candidate36,37,38,39,40, due to its easy and reproducible synthesis, combined with its relatively high ceramic yield and high purity. Moreover, the B/N ratio within the polymer is ideal to get further stoichiometric h-BN and there is no contaminant except hydrogen atoms that are easily removed during the ceramization step. In other words, the hexagonal arrangement of h-BN is already present within the molecular precursor’s structure in the borazinic ring. Further developments have shown that an incorporation of lithium nitride as crystallization promoter into the polymeric precursor noticeably improves, from outstandingly low temperatures (1000 °C), both the crystallization rate and the crystallinity level41. Recently, we have also demonstrated that, without any sintering step, a simple and classical resistive thermal treatment (<1200 °C) of this additivated preceramic polymer led to a highly crystallized h-BN, prone to be easily exfoliated to h-BN graphene like few layers42. In this previous study, the obtained BNNSs displayed size of couple of micrometers, which is not enough to envisage the above-mentioned applications.

The preceramisation process gives rise to an amorphous BN powder. With the purpose to favour crystallisation and increase crystals size, powder is then sintered by SPS43. Traditionally, SPS is used to get very dense material. Compared to conventional sintering techniques, near-theoretical density is indeed achieved at lower sintering temperature and for shorter treatment durations44. Even if the SPS process is most often applied for a densification purpose, it is known that its parameters45 (current pulse, pressure, heating rate) may also influence nucleation-growth mechanisms46. It is reasonable to assume that the intense pulse current lines generated during the SPS process may modify the crystallization step promoting the crystals growth. In that direction, the synergy between PDCs and SPS is a promising and accessible strategy to get pure, large h-BN flakes. The targeted BNNSs could then result in a subsequent exfoliation step.

Liquid PBN is first mixed with Li3N micro powder (5 wt. %) and preceramized at 650 °C prior to be sintered in the SPS apparatus. After 1 h under optimized experimental conditions (90 MPa pressure, 1800 °C, constant current of 770 A, 10 ms pulses ON and 5 ms OFF, vacuum in the SPS chamber of 0.15 mbar) a white pellet of 1 cm in diameter is obtained (Fig. 1a inset). A preliminary characterization of the chemical bonding within the specimen is investigated by X-ray photoelectron spectroscopy (XPS). Two analyses are performed on the same sample before and after an Ar+ sputtering of the surface, leading to 1 μm depth abrasion. Both general surveys appear on Fig. 2. Photoelectron peaks from B1s, N1s, O1s and C1s are clearly recognized in the spectrum recorded on the raw sample, giving an elemental chemical composition of 42.5; 43.6; 2.4 and 11.5%at., respectively. The binding energies of the B1s and N1s, at 190.7 eV and 398.6 eV, respectively, are consistent with reported XPS data for BN47. Both peaks are perfectly symmetric, confirming that B and N atoms are exclusively involved in BN bonds48,49. Moreover, the carbon peak at 285.0 eV, attributed to a pollution source, is very common with XPS measurements. The asymmetric shape of the C1s peak, typical of carbon pollution, still emphasizes this interpretation50. In the same way presence of the slight amount of oxygen (signal at 532.7 eV) would be linked to an oxygen impurity probably resulting from residual water traces or from oxygen adsorbed at the sample surface. However, this first analysis gives an elemental B/N ratio of 0,97, i.e. very close to the one of stoichiometric BN. The second analysis performed after abrasion (4 keV Ar+ sputtering), allows confirming that carbon and oxygen resulted from extrinsic pollution since they are almost absent in the sample (<0.5%at. for O1s and 1.3%at. for C1s). After etching, determination of the B/N ratio is more complicated since a preferential sputtering of nitrogen atoms occurs, leaving behind a boron-rich surface (54.6%at. for B1s vs 44.1%at. for N1s)51.

(a) SEM image showing stacked layers with micrometric sizes, inset: 1 cm-diameter pellet; (b) SEM image showing the pellet cross section and BNNSs aligned perpendicularly to the surface pellet; (c) Raman scattering spectrum recorded on the raw sample and (d) XRD patterns obtained with the raw sample (upper) analysis of the pellet surface and (bottom) analysis of the pellet cross-section.

(a) XPS general surveys obtained on the raw sample (1) and after 1-μm abrasion (2); (b) B1s peak and the corresponding deconvolution recorded on the raw sample; (c) N1s peak and the corresponding deconvolution recorded on the raw sample; (d) C1s peak and the corresponding deconvolution recorded on the raw sample and (e) O1s peak and the corresponding deconvolution recorded on the raw sample.

The as-sintered sample is then characterized adopting a multiscale approach (Scanning Electron Microscopy (SEM), Raman spectroscopy and X-Ray Diffraction). Figure 1a presents a representative SEM image recorded on the raw sample. It clearly shows very large and homogenous BN domains (up to 30 μm) well staked into differentiated flakes. If the pristine bulk pellet is clearly polycrystalline, we will show that each flake is a single crystal. Furthermore, it can be highlighted that BN flakes have a preferential orientation perpendicularly to the pellet surface e.g. aligned in the compressed direction (Fig. 1b). Figure 1c presents the Raman spectrum recorded on the raw sample. It is well known that Raman peak position and Full Width at Half Maximum (FWHM) are both parameters relative to crystallinity level of the sample. We can observe a well-defined single peak at 1366 ± 1 cm−1, which is characteristic of the E2g vibration mode of h-BN crystal40. This value is very close to the theoretical one reported for h-BN bulk material at 1367 cm−1 52. The slight difference with the bulk reference material is due to residual inter and/or intragranular stresses developed into the pellet and may result from the high energetic sintering process. This peak is symmetric with a FWHM of 7.7 cm−1. To the best of our knowledge, such a value is comparable to the one reported for the best h-BN single crystals obtained by HPHT9,10,53,54. This result is correlated with a very low defect density and a very large crystallite size. Figure 1d presents two XRD patterns performed on the raw sample. The upper spectrum is an X-Ray analysis of the pellet surface and the other one is an X-ray analysis of the pellet cross-section. Both patterns exhibit thin, intense and well-separated peaks indicating a good structural ordering. All peaks have been assigned to expected crystallographic planes from an h-BN crystal according to the JCPDS file number 01-073-2095 (Table 1). The comparison of both patterns clearly shows a drastic decrease of the intensity of all peaks except the {001} ones pointing out a preferential orientation of the h-BN crystallites along the a axis (characteristic of the covalent B-N bond) parallel to the applied load.

In summary, large micrometers-crystallized domains (up to 30 μm) grew in the sintering load direction, thus validating our method strategy based on the coupling of PDCs and SPS methods.

For a finer scale investigation, the h-BN raw pellet was scrubbed and mechanically exfoliated by the tape method, leading to 10 to 200 nm thick pieces with side size up to 30 μm (Fig. 3b). These BNNSs were deposited on a Si substrate, covered by a 80 nm SiO2 oxide layer in order to be characterized by Raman spectroscopy. Two spectra were recorded on two different BNNSs of the same sample differentiated by their contrast under optical microscope (Fig. 3a,b). Both spectra, shown in Fig. 3c, display the single peak of h-BN located at 1366 cm−1 with different intensities in relation to different BNNSs thicknesses. By AFM (Fig. 3c, inset), their thicknesses were measured at 13 nm and 114 nm. This result shows that mechanical exfoliation of h-BN leads to micrometric BNNSs of thicknesses down to few nanometers. Furthermore, the high crystalline quality of BNNS flakes is also confirmed by TEM (Fig. 4). Indeed, diffraction pattern associated with 5–30 μm BNNSs exhibited clearly hexagonal bright dots, which are representative of single crystals.

(a,b) optical images of BNNSs with different thicknesses deposited on Si02 surface and (c) Raman spectra recorded on the corresponding BNNSs, inset: AFM image obtained on the thicker sample.

TEM BF-image showing a large crystal and its corresponding diffraction pattern (inset).

Finally, in order to perform a deeper structural investigation, single crystal flakes can be easily isolated into thinner BNNS by an appropriate ultrasonic exfoliation treatment in ethanol. We have studied the crystal and BNNSs size distribution, respectively before and after the chemical exfoliation, from SEM and optical images (see Supplementary Fig. S1 online). It is worth mentioning that such a size could still be increased by optimizing the exfoliation process. Figure 5 presents a TEM image recorded on an isolated BNNS measuring 10 to 15 μm. After exfoliation, their thickness slows down to several nanometers, which is approaching the targeted structure of graphene-like two-dimensional sheets. Then, the flatness of the BNNSs has been investigated by AFM (see Supplementary Fig. S2 online). In a typical study, the RMS (Root Mean Square) roughness has been determined to 0.7 nm. This value is similar to the one measured for standard silica. Even if we did not observe a lower value as it was shown in the work of Dean et al.55 we reasonably think that the flatness of our samples would be compatible with graphene deposition as substrate or to produce van der Waals heterostructures. Figure 6a shows homogeneous crystalline areas with Moiré patterns on extended zones confirming the high level of crystallinity. The selective area electron diffraction (SAED) pattern (Fig. 6b, inset), obtained from the high resolution image (Fig. 6b), shows six bright spots hexagonally distributed demonstrating the achievement of h-BN single crystals. This corresponding SAED pattern can be interpreted as the AA’ atomic stacking in the c-direction. Atomic layers can also be stacked in a more complex turbostratic structure, as demonstrated by the hexagonal-shaped Moiré patterns obtained on different samples area (Fig. 6c–e). Misorientations between h-BN layers similar to graphene can explain those Moiré patterns, which reveal themselves by multiple spots in corresponding Fast Fourier Transform images (Fig. 6c–e inset)56. Those images show two sets of hexagonal spots rotated with angles of 12°, 21° and 25° respectively. By modelling these misorientations with two BN monolayers, it is possible to match quite well corresponding FFT images (Fig. 6f–h). This relative rotation could be due to the stain induced by rolled structure, as already imaged for rotational stacking fault in few-layer graphene sheets57.

TEM BF-image showing a 10 μm BNNS and its corresponding diffraction pattern (inset).

(a) BF-TEM micrograph of large h-BN sheets (10 μm) with Moiré patterns. Three misorientated single crystals were delimitated with dashed line; (b) typical hexagonal atomic arrangement of h-BN few layers, inset: corresponding SAED pattern; (c–e) particular atomic arrangement exhibiting hexagonal shaped Moiré patterns with angles misorientation of 12°, 21° and 25°, insets: corresponding FFT images; (f–h) modeling of two h-BN layers rotated of corresponding angles.

In order to get further information about the chemical composition, analysis by electron energy loss spectroscopy (EELS) was directly performed on thin BNNSs (Fig. 7). Only boron and nitrogen K-edges are recorded while no traces of lithium, carbon or oxygen is detected. This supplementary chemical analysis corroborates previous XPS results concluding on the excellent purity of samples: bulk, as well as BNNSs.

(a) Wide range EELS spectrum obtained on a BNNS, inset: high resolution spectra of B and N K-edge; (b) high resolution spectrum acquired around the K-edge of Li; (c) high resolution spectrum acquired around the K-edge of C and (d) high resolution spectrum acquired around the K-edge of O.

To summarize, the novelty of the method comes from the association of two synthesis processes: the PDCs route which is known to lead to high purity ceramic when a pure preceramic polymer is used and the SPS one that allows reaching high crystallinity to the final ceramic. The beneficial effect of SPS is obvious when comparing characteristics of the present BNNSs with the best ones synthesized by a single PDCs route42. For instance the crystalline quality is first significantly improved as shown by the FWHM Raman peaks measurement that decreased from 40 cm−1 for PDCs BNNSs to 7.7 cm−1 for the PDCs-SPS’BNNSs. Moreover, we demonstrated that applying an external current (by SPS) led to preferentially orientated flakes with much larger domains (up to 30 μm) than the ones obtained previously (1–2 μm). On the other hand, even if the NIMS laboratory may bring to the scientific community larger crystals (500 μm), their experimental procedure is more energy and time consuming. Indeed, it can be underlined that to reach GPa pressure conditions, a specific and dedicated instrument (diamond anvil) is required, which limits the entire size of the sample and is not easy to access. Summarized comparative data are gathered as Supplementary Table S2 online.

Finally, the quality of our samples may open new perspectives for many applications as graphene substrate or to produce van der Waals heterostructures.

To conclude, we have demonstrated that a large amount of self-standing h-BN few-layers can be obtained by exfoliation of highly crystallized h-BN bulk material, the latter being prepared using a relevant dual synthesis method involving the PDCs route and the SPS process. This original method offers a new alternative way to generate high quality h-BN crystals as new source of supply for BBNSs.

A dispersion of lithium nitride (Li3N, Aldrich) micro powders (5 wt%) in liquid polyborazilene (PBN), was prepared following a procedure described elsewhere42. This dispersion was slowly heated in a Schlenk tube under argon from room temperature to 200 °C and held at 200 °C for 1 h leading to a solid-state polymer avoiding further oligomer evaporation. The obtained white powder (82% mass yield) was then placed into an alumina crucible to be heated under N2 at 650 °C (1 °C.min−1) and kept at this final temperature for 1 h. In a gloves box, the SPS graphite die covered with a papyex® was filled with the preceramic powder and then transferred into the SPS chamber (HP D 25, FCT System) in-between the two punches and compressed at room temperature under uniaxial load until 90 MPa. SPS heating (10 ms pulses ON and 5 ms OFF) was then conducted up to 1800 °C keeping the normal load constant. During the 1 h dwell temperature the current was 770A and the vacuum in the SPS chamber was 0.15 mbar. The annealing process was held at this maximum temperature to complete the BN ceramization reaction and the densification process. Removing the protective papyex, a white pellet (300 mg) was finally obtained. SEM observations were carried out at very low accelerating voltage (200 V) using a SUPRA Zeiss microscope. Raman spectra were acquired in a Horiba Jobin-Yvon ARAMIS spectrometer equipped with a 1800 lines/nm grating, using an excitation wavelength of 532 nm and a x50 objective (the main Raman band of the silica peak is located at 520.1 cm−1). XPS measurements were done using a PHI Quantera SXM instrument equipped with a 180 hemispherical electron energy analyzer and a monochromatized Al Kα (1486.6 eV) source operated at 15 kV and 4 mA. Analyses were performed on the raw sample and after a 1 μm abrasion using a 4 keV Ar+ sputtering. XRD patterns were recorded with a Phillips PW 1830/40 diffractometer, with a CuK radiation source. BNNSs are then prepared by chemical (in ethanol, ultrasonication: 1 min at 25 W, Hielscher UP400S and centrifugation) or physical (tape) exfoliation. A droplet of the solution was simply deposited onto a 300 mesh holey carbon copper grid in order to perform TEM observations (JEOL 2100F and 2010F microscopes operating at 200 kV). EELS spectra were recorded using a JEOL JEM-ARM200F Cold FEG, operating at 200 kV.

How to cite this article: Yuan, S. et al. Pure & crystallized 2D Boron Nitride sheets synthesized via a novel process coupling both PDCs and SPS methods. Sci. Rep. 6, 20388; doi: 10.1038/srep20388 (2016).

Lee, G.-H. et al. Electron tunneling through atomically flat and ultrathin hexagonal boron nitride. Appl. Phys. Lett. 99, 243114–243116 (2011).

Article ADS CAS Google Scholar

Golberg, D. et al. Boron Nitride Nanotubes and Nanosheets. ACS Nano 4, 2979–2993 (2010).

Article CAS PubMed Google Scholar

Britnell, L. et al. Field-Effect Tunneling Transistor Based on Vertical Graphene Heterostructures. Science 335, 947–950 (2012).

Article ADS CAS PubMed Google Scholar

Mehr, W. et al. Vertical Graphene Base Transistor. IEEE Electron Device Lett. 33, 691–693 (2012).

Article ADS CAS Google Scholar

Liu, Z. et al. In-plane heterostructures of graphene and hexagonal boron nitride with controlled domain sizes. Nat. Nanotechnol. 8, 119–124 (2013).

Article ADS CAS PubMed Google Scholar

Song, L. et al. Large scale growth and characterization of atomic hexagonal boron nitride layers. Nano Lett. 10, 3209–3215 (2010).

Article ADS CAS PubMed Google Scholar

Clere, T. M. Method for making high thermal diffusivity boron nitride powders. United State patent US 7189774 B2. 2007 March 13.

Lin, K. Y., Raman, C., Xiang, B. & Murugaiah, A. Composition comprising exfoliated boron nitride and method for forming such compositions. United State patent US 20140077125 A1. 2014 march 20.

Watanabe, K., Taniguchi, T. & Kanda, H. Direct-bandgap properties and evidence for ultraviolet lasing of hexagonal boron nitride single crystal. Nat. Mater. 3, 404–409 (2004).

Article ADS CAS PubMed Google Scholar

Kubota, Y., Watanabe, K., Tsuda, O. & Taniguchi, T. Deep Ultraviolet Light-Emitting Hexagonal Boron Nitride Synthesized at Atmospheric Pressure. Science 317, 932–934 (2007).

Article ADS CAS PubMed Google Scholar

Guo, N. et al. Fabrication of large area hexagonal boron nitride thin films for bendable capacitors. Nano Res. 6, 602–610 (2013).

Article CAS Google Scholar

Kim, E., Jain, N., Jacobs-Gedrim, R., Xu, Y. & Yu, B. Exploring carrier transport phenomena in a CVD-assembled graphene FET on hexagonal boron nitride. Nanotechnology 23, 125706–125710 (2012).

Article ADS PubMed CAS Google Scholar

Liu, Z. et al. Direct Growth of Graphene/Hexagonal Boron Nitride Stacked Layers. Nano Lett. 11, 2032–2037 (2011).

Article ADS CAS PubMed Google Scholar

Gibb, A. L. et al. Atomic Resolution Imaging of Grain Boundary Defects in Monolayer Chemical Vapor Deposition-Grown Hexagonal Boron Nitride. J. Am. Chem. Soc. 135, 6758–6761 (2013).

Article CAS PubMed Google Scholar

Ismach, A. et al. Toward the Controlled Synthesis of Hexagonal Boron Nitride Films. ACS Nano 6, 6378–6385 (2012).

Article CAS PubMed Google Scholar

Corso, M. et al. Boron Nitride Nanomesh. Science 303, 217–220 (2004).

Article ADS CAS PubMed Google Scholar

Simonson, R. J., Paffett, M. T., Jones, M. E. & Koel, B. E. A vibrational study of borazine adsorbed on Pt(111) and Au(111) surfaces. Surf. Sci. 254, 29–44 (1991).

Article ADS CAS Google Scholar

Preobrajenski, A. B., Nesterov, M. A., Ng, M. L., Vinogradov, A. S. & Mårtensson, N. Monolayer h-BN on lattice-mismatched metal surfaces: On the formation of the nanomesh. Chem. Phys. Lett. 446, 119–123 (2007).

Article ADS CAS Google Scholar

Sutter, P., Lahiri, J., Albrecht, P. & Sutter, E. Chemical Vapor Deposition and Etching of High-Quality Monolayer Hexagonal Boron Nitride Films. ACS Nano 5, 7303–7309 (2011).

Article CAS PubMed Google Scholar

Novoselov, K. S. et al. Two-dimensional atomic crystals. Proc. Natl. Acad. Sci. U. S. A. 102, 10451–10453 (2005).

Article ADS CAS PubMed PubMed Central Google Scholar

Li, L. H. et al. Large-scale mechanical peeling of boron nitride nanosheets by low-energy ball milling. J. Mater. Chem. 21, 11862–11866 (2011).

Article CAS Google Scholar

Pacilé, D., Meyer, J. C., Girit, Ç. Ö. & Zettl, A. The two-dimensional phase of boron nitride: Few-atomic-layer sheets and suspended membranes. Appl. Phys. Lett. 92, 133107–133109 (2008).

Article ADS CAS Google Scholar

Meyer, J. C., Chuvilin, A., Algara-Siller, G., Biskupek, J. & Kaiser, U. Selective Sputtering and Atomic Resolution Imaging of Atomically Thin Boron Nitride Membranes. Nano Lett. 9, 2683–2689 (2009).

Article ADS CAS PubMed Google Scholar

Gorbachev, R. V. et al. Hunting for Monolayer Boron Nitride: Optical and Raman Signatures. Small 7, 465–468 (2011).

Article CAS PubMed Google Scholar

Han, W.-Q., Wu, L., Zhu, Y., Watanabe, K. & Taniguchi, T. Structure of chemically derived mono- and few-atomic-layer boron nitride sheets. Appl. Phys. Lett. 93, 223103–223105 (2008).

Article ADS CAS Google Scholar

Warner, J. H., Rümmeli, M. H., Bachmatiuk, A. & Büchner, B. Atomic Resolution Imaging and Topography of Boron Nitride Sheets Produced by Chemical Exfoliation. ACS Nano 4, 1299–1304 (2010).

Article CAS PubMed Google Scholar

Zhi, C., Bando, Y., Tang, C., Kuwahara, H. & Golberg, D. Large-Scale Fabrication of Boron Nitride Nanosheets and Their Utilization in Polymeric Composites with Improved Thermal and Mechanical Properties. Adv. Mater. 21, 2889–2893 (2009).

Article CAS Google Scholar

Lin, Y., Williams, T. V. & Connell, J. W. Soluble, Exfoliated Hexagonal Boron Nitride Nanosheets. J. Phys. Chem. Lett. 1, 277–283 (2010).

Article CAS Google Scholar

Yurdakul, H. et al. Nanoscopic characterization of two-dimensional (2D) boron nitride nanosheets (BNNSs) produced by microfluidization. Ceram. Int. 38, 2187–2193 (2012).

Article CAS Google Scholar

Li, X. et al. Exfoliation of Hexagonal Boron Nitride by Molten Hydroxides. Adv. Mater. 25, 2200–2204 (2013).

Article CAS PubMed Google Scholar

Chen, X., Dobson, J. F. & Raston, C. L. Vortex fluidic exfoliation of graphite and boron nitride. Chem. Commun. 48, 3703–3705 (2012).

Article CAS Google Scholar

Yi, M. et al. Hydrodynamics-assisted scalable production of boron nitride nanosheets and their application in improving oxygen-atom erosion resistance of polymeric composites. Nanoscale 5, 10660–10667 (2013).

Article ADS CAS PubMed Google Scholar

Jan, R. et al. Enhancing the mechanical properties of BN nanosheet–polymer composites by uniaxial drawing. Nanoscale 6, 4889–4895 (2014).

Article ADS CAS PubMed Google Scholar

Yi, M., Shen, Z., Liu, L. & Liang, S. Size-selected boron nitride nanosheets as oxygen-atom corrosion resistant fillers. RSC Adv. 5, 2983–2987 (2014).

Article ADS CAS Google Scholar

Liu, L. et al. Boron nitride nanosheets with controlled size and thickness for enhancing mechanical properties and atomic oxygen erosion resistance. RSC Adv. 4, 37726–37732 (2014).

Article CAS ADS Google Scholar

Kusari, U. et al. Formation of nanostructured, nanocrystalline boron nitride microparticles with diatom-derived 3-D shapes. Chem. Commun. 1177–1179 (2007), doi: 10.1039/B614494B.

Zhong, W. et al. Design of carbon fiber reinforced boron nitride matrix composites by vacuum-assisted polyborazylene transfer molding and pyrolysis. J. Eur. Ceram. Soc. 33, 2979–2992 (2013).

Article CAS Google Scholar

Termoss, H. et al. Preparation of boron nitride-based coatings on metallic substrates via infrared irradiation of dip-coated polyborazylene. J. Mater. Chem. 19, 2671–2674 (2009).

Article CAS Google Scholar

Li, J., Bernard, S., Salles, V., Gervais, C. & Miele, P. Preparation of Polyborazylene-Derived Bulk Boron Nitride with Tunable Properties by Warm-Pressing and Pressureless Pyrolysis. Chem. Mater. 22, 2010–2019 (2010).

Article CAS Google Scholar

Yuan, S. et al. New potential for preparation of performing h-BN coatings via polymer pyrolysis in RTA furnace. J. Eur. Ceram. Soc. 33, 393–402 (2013).

Article CAS Google Scholar

Yuan, S. et al. Low-Temperature Synthesis of Highly Crystallized Hexagonal Boron Nitride Sheets with Li3N as Additive Agent. Eur. J. Inorg. Chem. 2014, 5507–5513 (2014).

Article CAS Google Scholar

Yuan, S., Toury, B., Journet, C. & Brioude, A. Synthesis of hexagonal boron nitride graphene-like few layers. Nanoscale 6, 7838–7841 (2014).

Article ADS CAS PubMed Google Scholar

Bernard, S. & Miele, P. Ordered mesoporous polymer-derived ceramics and their processing into hierarchically porous boron nitride and silicoboron carbonitride monoliths. New J. Chem. 38, 1923–1931 (2014).

Article CAS Google Scholar

Munir, Z. A., Quach, D. V. & Ohyanagi, M. Electric Current Activation of Sintering: A Review of the Pulsed Electric Current Sintering Process. J. Am. Ceram. Soc. 94, 1–19 (2011).

Article CAS Google Scholar

Aman, Y., Garnier, V. & Djurado, E. A Screening Design Approach for the Understanding of Spark Plasma Sintering Parameters: A Case of Translucent Polycrystalline Undoped Alumina. Int. J. Appl. Ceram. Technol. 7, 574–586 (2010).

Article CAS Google Scholar

Omori, M. Sintering, consolidation, reaction and crystal growth by the spark plasma system (SPS). Mater. Sci. Eng. A 287, 183–188 (2000).

Article Google Scholar

Moulder, J., Stickle, W., Sobol, P. & Bomben, K. Handbook of X-ray Photoelectron Spectroscopy. (ed. Chastain, J. ) (Perkin-Elmer Corp: Eden Prairie, 1992).

Saitoh, H., Yoshida, K. K. & Yarbrough, W. A. Preparation and characterization of boron rich boron nitride microcrystals by hot filament assisted chemical vapor deposition. J. Chem. Vap. Depos. 1, 59 (1992).

CAS Google Scholar

Patibandla, N. & Luthra, K. L. Chemical Vapor Deposition of Boron Nitride. J. Electrochem. Soc. 139, 3558–3565 (1992).

Article CAS ADS Google Scholar

Vincent, H. et al. Microtexture and structure of boron nitride fibres by transmission electron microscopy, X-ray diffraction, photoelectron spectroscopy and Raman scattering. Mater. Sci. Eng. A 340, 181–192 (2003).

Article Google Scholar

Guimon, C. et al. XPS study of BN thin films deposited by CVD on SiC plane substrates. Surf. Interface Anal. 16, 440–445 (1990).

Article CAS Google Scholar

Nemanich, R. J., Solin, S. A. & Martin, R. M. Light scattering study of boron nitride microcrystals. Phys. Rev. B 23, 6348–6356 (1981).

Article ADS CAS Google Scholar

Clubine, B. Synthesis and characterization of bulk single crystal hexagonal boron nitride from metal solvents. 35 (Kansas State University, 2012).

Watanabe, K., Taniguchi, T. & Kanda, H. Ultraviolet luminescence spectra of boron nitride single crystals grown under high pressure and high temperature. Phys. Status Solidi A 201, 2561–2565 (2004).

Article ADS CAS Google Scholar

Dean, C. R. et al. Boron nitride substrates for high-quality graphene electronics. Nat. Nanotechnol. 5, 722–726 (2010).

Article ADS CAS PubMed Google Scholar

Zan, R., M., Q., Jalil, R. & Bangert, U. Advances in Graphene Science (ed. Aliofkhazraei, M. ) 3–30 (InTech, 2013).

Warner, J. H., Rümmeli, M. H., Gemming, T., Büchner, B. & Briggs, G. A. D. Direct Imaging of Rotational Stacking Faults in Few Layer Graphene. Nano Lett. 9, 102–106 (2009).

Article ADS CAS PubMed Google Scholar

Download references

Authors gratefully acknowledge the ANR for its financial support through the project 14-CE08-0018 «GoBN», the CTμ (Centre Technologique des Microstructures) of the Université Lyon 1 and CLYM (Centre Lyonnais de Microscopie) for access to TEMs.

Laboratoire des Multimatériaux et Interfaces, CNRS, UMR 5615, Université Lyon 1, Université de Lyon, Villeurbanne, F-69622, France

Sheng Yuan, Sébastien Linas, Catherine Journet, Arnaud Brioude & Bérangère Toury

Matériaux Ingénierie et Science, UMR CNRS 5510, INSA de Lyon, Université de Lyon, Villeurbanne, F- 69621, France

Sheng Yuan, Philippe Steyer, Vincent Garnier & Guillaume Bonnefont

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

S.Y. and B.T. produced the PBN by PDCs and conducted the measurements by XRD, V.G. and G.B. conducted the SPS process. C.J., A.B. and P.S. performed the SEM and TEM characterization. S.L. characterized the samples by AFM and Raman spectroscopy. All authors contributed to write the paper.

The authors declare no competing financial interests.

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

Reprints and Permissions

Yuan, S., Linas, S., Journet, C. et al. Pure & crystallized 2D Boron Nitride sheets synthesized via a novel process coupling both PDCs and SPS methods. Sci Rep 6, 20388 (2016). https://doi.org/10.1038/srep20388

Download citation

Received: 11 October 2015

Accepted: 31 December 2015

Published: 04 February 2016

DOI: https://doi.org/10.1038/srep20388

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Applied Nanoscience (2020)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.